| 合金牌號 | 化學(xué)成分/% | |||||||||
| Cu | Si | Mg | Zn | Fe | Mn | Ni | Sn | Pb | Al | |
| ADC1 | ＜1.0 | 11.0~13.0 | ＜0.3 | ＜0.5 | ＜1.3 | ＜0.3 | ＜0.5 | ＜0.1 | ＜0.20 | 余量 |
| ADC3 | ＜0.6 | 9.0~11.0 | 0.4~0.6 | ＜0.5 | ＜1.3 | ＜0.3 | ＜0.5 | ＜0.1 | ＜0.15 | 余量 |
| ADC5 | ＜0.2 | ＜0.3 | 4.0~8.5 | ＜0.1 | ＜1.8 | ＜0.3 | ＜0.1 | ＜0.1 | ＜0.10 | 余量 |
| ADC6 | ＜0.1 | ＜1.0 | 2.5~4.0 | ＜0.4 | ＜0.8 | ＜0.4~0.6 | ＜0.1 | ＜0.1 | ＜0.10 | 余量 |
| ADC10 | 2.0~4.0 | 7.5~9.5 | ＜0.3 | ＜1.0 | ＜1.3 | ＜0.5 | ＜0.5 | ＜0.2 | ＜0.2 | 余量 |
| ADC10Z | 2.0~4.0 | 7.5~9.5 | ＜0.3 | ＜3.0 | ＜1.3 | ＜0.5 | ＜0.5 | ＜0.2 | ＜0.2 | 余量 |
| ADC12 | 1.5~3.5 | 9.6~12.0 | ＜0.3 | ＜1.0 | ＜1.3 | ＜0.5 | ＜0.5 | ＜0.2 | ＜0.2 | 余量 |
| ADC12Z | 1.5~3.5 | 9.6~12.0 | ＜0.3 | ＜3.0 | ＜1.3 | ＜0.5 | ＜0.5 | ＜0.2 | ＜0.2 | 余量 |
| ADC14 | 4.0~5.0 | 16.0~18.0 | 0.45~0.65 | ＜1.5 | ＜1.3 | ＜0.5 | ＜0.3 | ＜0.3 | ＜0.2 | 余量 |
日本的鑄造鋁合金化學(xué)成分標(biāo)準
| 合金牌號 | 化學(xué)成分/% | ||||||||
| Cu | Si | Mg | Zn | Fe | Mn | Ni | Ti | Al | |
| AC1B | 4.2~5.0 | ＜0.3 | 0.15~0.35 | ＜0.1 | ＜0.35 | ＜0.1 | ＜0.05 | 0.05~0.35 | 余量 |
| AC2A | 3.0~4.5 | 4.0~6.0 | ＜0.25 | ＜0.55 | ＜0.8 | ＜0.55 | ＜0.30 | ＜0.20 | 余量 |
| AC2B | 2.0~4.0 | 5.0~7.0 | ＜0.50 | ＜1.0 | ＜1.0 | ＜0.50 | ＜0.35 | ＜0.20 | 余量 |
| AC3A | ＜0.25 | 10.0~13.0 | ＜0.15 | ＜0.30 | ＜0.8 | ＜0.35 | ＜0.10 | ＜0.20 | 余量 |
| AC4A | ＜0.25 | 8.0~10.0 | 0.30~0.6 | ＜0.25 | ＜0.55 | ＜0.30~0.6 | ＜0.10 | ＜0.20 | 余量 |
| AC4B | 2.0~4.0 | 7.0~10.0 | ＜0.50 | ＜1.0 | ＜1.0 | ＜0.50 | ＜0.35 | ＜0.20 | 余量 |
| AC4C | ＜0.20 | 6.5~7.5 | 0.20~0.4 | ＜0.3 | ＜0.5 | ＜0.6 | ＜0.05 | ＜0.20 | 余量 |
| AC4CHa) | ＜0.10 | 6.5~7.5 | 0.25~0.45 | ＜0.10 | ＜0.20 | ＜0.10 | ＜0.05 | 0.2 | 余量 |
| AC4D | 1.0~1.5 | 4.5~5.5 | 0.4~0.6 | ＜0.5 | ＜0.6 | ＜0.5 | ＜0.3 | ＜0.2 | 余量 |
| AC5A | 3.5~4.5 | ＜0.7 | 1.2~1.8 | ＜0.1 | ＜0.7 | ＜0.6 | 1.7~2.3 | ＜0.2 | 余量 |
| AC7A | ＜0.10 | ＜0.20 | 3.5~5.5 | ＜0.15 | ＜0.30 | ＜0.6 | ＜0.05 | ＜0.20 | 余量 |
| AC8A | 0.8~1.3 | 11.0~13.0 | 0.7~1.3 | ＜0.15 | ＜0.8 | ＜0.15 | 0.8~1.5 | ＜0.20 | 余量 |
| AC8B | 2.0~4.0 | 8.5~10.5 | 0.50~1.5 | ＜0.50 | ＜1.0 | ＜0.50 | 0.10~1.0 | ＜0.20 | 余量 |
| AC8C | 2.0~4.0 | 8.5~10.5 | 0.50~1.5 | ＜0.50 | ＜1.0 | ＜0.50 | ＜0.50 | ＜0.20 | 余量 |
| AC9A | 0.50~1.5 | 22~24 | 0.50~1.5 | ＜0.20 | ＜0.8 | ＜0.50 | 0.50~1.5 | ＜0.20 | 余量 |
| AC9B | 0.50~1.5 | 18~20 | 0.50~1.5 | ＜0.20 | ＜0.8 | ＜0.50 | 0.50~1.5 | ＜0.20 | 余量 |
公司可生產(chǎn)定制ADC系列壓鑄鋁合金圓棒級大板錠，提高產(chǎn)品品質(zhì)，替代日本進口及市場上采用廢舊鋁再生并壓鑄成型產(chǎn)品。目前可供應(yīng)直徑規(guī)格Φ88~350mm的圓棒和寬度730mm的大板錠，產(chǎn)品表面光潔，內(nèi)部的氣孔、夾渣等缺陷比傳統(tǒng)壓鑄產(chǎn)品大幅減少，組織晶粒進一步細化。經(jīng)過對機械性能、微觀組織等進行分析測試表明，該材料的強度和延伸率等指標(biāo)均優(yōu)于國內(nèi)的ADC壓鑄鋁合金產(chǎn)品，其中強度提高約10~15%，延伸率提高約20~30%，可滿足汽車、動車等領(lǐng)域?qū)Ω咝阅懿牧系男枨蟆?/p>